The structural, optical and photocatalytic properties of $TiO_2$ thin films fabricated by do magnetron sputtering

직류 마그네트론 스퍼터링법으로 제조된 $TiO_2$ 박막의 구조적, 광학적 특성 및 광촉매 효과

[ $TiO_2$ ] thin films were fabricated by DC magnetron sputtering system at by controlling deposition times, ratios of $Ar:O_2$ partial presser ratio and substrate conditions. And the surface, cross-section morphology, microstructure, and composition ratio of the films were analyzed by FE-SEM, TEM and XPS. Besides, the optical absorption and transmittance of the $TiO_2$ films were measured by a UV-VIS-NIR Spectrophotometer, and photocatalytic properties were studied by G C Analyzer & Data Analysis system. As the result, when $TiO_2$ thin film was made at deposition time of 120[min] and $Ar:O_2$ ratio of 60:40, the best structural and optical properties among many thin films could be accepted. The best results of properties were as follows: thickness; $360{\sim}370[nm]$, grain size; 40[m], gap between two peak binding energy, $5.8{\pm}0.05[eV]$ ($2p_{3/2}$ peak and $2p_{1/2}$ peak of Ti was show at $458.3{\pm}0.05[eV]$ and $464.1{\pm}0.05[eV]$ respectively), binding energy; $530{\pm}0.05\;[eV]$, opticalenergy band gap; 3.4[eV].