Preparation of High density YIG ferrite by conventional solid-state sintering

고상합성법에 의한 고밀토 YIG 자성체 제조

YIG(Yttrium Iron Garnet) is one of the most widely used ferrites for microwave telecommunication. It used as a passive devices such as isolators and circulators. In order to reduce the insertion losses of these passive devices, it is very important to reduce magnetic loss of the ferrites. In general, the magnetic losses of ferrites is closely related to the microstructure of the ceramics. In the sintering of YIG, pores are easily trapped in grains and grain boundaries. These pores cause to increase magnetic losses of the sinterted bodies. In this paper, the effect of the $SiO_2$ addition on the microstructure was discussed. Increasing the $SiO_2$ addition, the grain size was reduced, which means that added acts as a grain-growth inhibitor. During the sintering, $SiO_2$ settled down on the grain boundaries, and drag the grain growth. Therefore, there is enough time for pores to move out. The relative density of YIG sintered at $1350^{\circ}C$ with 1 mol% $SiO_2$ addition was 99.6%. $\Delta$H of these samples was under 50 Oe.