Ferroelectric properties of BET Thin Films for FRAM

FRAM 응용을 위한 BET 박막의 강유전 특성

Ferroelectric europium-substitution $Bi_4Ti_3O_{12}$ thin films were fabricated by spin-coating onto a Pt/Ti/$SiO_2$/Si substrate. The $Bi_{3.25}Eu_{0.75}Ti_3O_{12}$ (BET) films have polycrystalline structure annealed at 700 C. We investigated that the influence of $Bi_4Ti_3O_{12}$ thin films by substituting for Bi ions with Bi ions using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). From the XPS measurement, it was suggested that the stability of the metal-oxygen octahedral should be related to substitute for Bi ions with Eu ions at annealed $800^{\circ}C$. The BET thin films showed a large remanent polarization (2Pr) of $60.99C/cm^2$ at an applied voltage of 10 V. The BET thin films exhibited no significant degradation of switching charge at least up to $5{\times}10^9$ switching cycles at a frequency of 50 kHz.