The effect of $SrSO_{4}$ on Bi2212 HTS tube

$SrSO_{4}$의 첨가량이 Bi2212 고온초전도체 튜브에 미치는 영향

  • Jung, Seng-Ho (Department of Materials Engineering, Chungbuk National University) ;
  • Jang, Gun-Eik (Department of Materials Engineering, Chungbuk National University)
  • Published : 2003.05.23
Download PDF
⟨ Previous Next ⟩

Abstract

$SrSO_4$ were systematically added on Bi2212 from 0 to 10wt% to study the effect of Bi2212 superconductor tube characteristics. After mixing, the melted solution of Bi2212 and $SrSO_4$ was initially poured into the cylinder type of steel mold preheated at $550^{\circ}C$ for 30min and rotated at 1000rpm. Following that, tube was annealed at $840^{\circ}C$ for 72hrs. The tube dimension was 60 in diameter, 60mm in length and 2mm in thickness. XRD data suggests that there was no typical segregation phase related with $SrSO_4$. Well textured grain with typical 2212 phase was observed and average size was $20{\mu}m$. The measured critical current and critical current density of Bi2212 tube added by 5% $SrSO_4$ at 77K were 495A and $202A/cm^2$ respectively.