Creep tests for Titan were carned out using constant-load at $600^{\circ}C$, $650^{\circ}C$ and $700^{\circ}C$. Material constants necessary to predict creep life were acquired from the experimental creep data. And the applicability of Monkman-Grant(M-G) and modified M-G relationships was discussed. It was discovered the log-log plot of M-G relationships between the rupure time(tr) and he minimum creep rate(${\varepsilon}_m$) was conditional on test temperatures. The slop of m was 2.75 at $600^{\circ}C$ and m was 1.92 at $700^{\circ}C$. However; the log-log plot of modified M-G relationships between $t_r/\varepsilon_r$ and $\varepsilon_m$ was indpendent on stresses and temperatures. That is the slop of m' was almost 3.90 in all the data. Thus, change M-G relationships to creep life prediction could be vtilized more reasonably than that of M-G relationships for type Titan. It was divided that the constant slopes never theless of temperatures of practical stresses in the modified relationship were due to an intergranular break grown by wedge-type cauities.