Brazing of TiAl and AISI4140 steel using an Ag-Cu-Ti insert metal

Ag-Cu-Ti삽입금속을 이용한 TiAl과 AISI4140 강의 브레이징

We have investigated the microstructures and the mechanical properties of TiA1/Cerameti1721 (Ag-Cu-Ti insert metal)/AISI4140 joints at 800$^{\circ}C$ for 60 to 300s using induction brazing method. Two continuous reaction layers of AICuTi and AICu$_2$Ti were formed at the interface between the braze and TiAl, whose thickness increased with the brazing time. The braze consisted of Ag-rich, Ti-rich, CuTi and CuTi$_2$ phases. The maximum tensile strength achieved 296MPa, which was 71% of that of TiAl base metal, for the specimen bonded at 800$^{\circ}C$. Further increase of the brazing temperature and time resulted in constant deterioration of its bonding strength due to large amount of brittle IMC.