형상에 따른 초전도 튜브의 전기적 특성변화

High-temperature Superconductor(HTS) tubes were fabricated in term of different diameter, length and thickness by centrigugal forming method. For powder melting by induction the optimum range of melting temperatures and preheating temperature were $1050^{\circ}C{\sim}1100^{\circ}C\;amd\;550^{\circ}C$ for 30min, respectively. The mould renting speed was 1000rpm. A tube was annealed at $840^{\circ}C$ for 72hours in oxygen atmosphere. The plate-like grains were well developed along the renting direction and typical grain size was about more than $40{\mu}m$. It was found that Ic values increased with increasing the tube diameter while the Ic decreased with increasing tube thickness. Also Ic decreased with increasing the tube length. The measured Ic in $50mm{\times}70mm{\times}25mm$ tube was about 896Amp.