Optical Properties for $CuGaTe_2/GaAs$ Epilayers Grown by Hot Wall Epilaxy

Hot Wall Epitaxy (HWE) 방법으로 성장된 $CuGaTe_2/GaAs$ 에피레이어의 광학적 특성

The stochiometric mix of evaporating materials for the $CuGaT_2$ single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuGaTe_2$ polycrystal, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were 6.025 ${\AA}$ and 11.931 ${\AA}$, respectively. To obtain the single crystal thin films, $CuGaTe_2$ mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $670^{\circ}C$ and $410^{\circ}C$ respectively, and the thickness of the single crystal thin films is $2.1{\mu}m$. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). From the photocurrent spectrum by illumination of perpendicular light on the c - axis of the $CuGaTe_2$ single crystal thin film, we have found that the values of spin orbit coupling ${\Delta}s.o$ and the crystal field splitting ${\Delta}cr$ were $0.079\underline{1}eV$ and $0.246\underline{3}eV$ at 10 K, respectively. From the PL spectra at 10K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be $0.047\underline{0}eV$ and the dissipation energy of the donor-bound exciton and acceptor-bound exciton to be $0.049\underline{0}eV$, $0.055\underline{8}eV$, respectively.