Abstract
Boron Phosphide films were deposited on (111) Si substrate at $650^{\circ}C$, by the reaction of $B_2H_6$ with PH, using APCVD. $N_2$ was carried out as carrier gas. The optimal gas rates were 20 ml/min for B2H6, 60 ml/min for PH3 and 1 l/min for N2. After as grown the films were insitu annealed fur 1hour in $N_2$ ambient at $550^{\circ}C$ and measured. The measurement of AFM shows that the average surface roughness is $10.108{\AA}$ for the reaction temperature at $450^{\circ}C$ and $29.626{\AA}$ fur the reaction temperature at $650^{\circ}C$. The measurement of XRD shows that the films have the orientation of(1 0 1). Also, the measurement of AES is shown that the films have $B_{13}P_2$ stoichiometry. For the Result of microwaves absorbtion properties using VNA, it obtained the permittivity of BP about 8 between $1.5{\sim}2.5GHz$. In this study, it obtained the BP thin film by deposited in atmosphere pressure And BP thin film can be after to applicate as microwave absolution material is obtained.