Effects of $B_2O_3$ Additives on the Sintering Temperature and Microwave Dielectric Properties of $Ba(Zn_{1/3}Nb_{2/3})O_3$ Ceramics

$B_2O_3$의 첨가가 $Ba(Zn_{1/3}Nb_{2/3})O_3$ 세라믹스의 소결 온도와 고주파 유전 특성에 미치는 영향

  • Kim, Min-Han (Department of Materials Science and Engineering, Korea University) ;
  • Son, Jin-Ok (Department of Materials Science and Engineering, Korea University) ;
  • Nahm, Sahn (Department of Materials Science and Engineering, Korea University) ;
  • Yoo, Myong-Jae (Korea Electronics Technology Institute, Korea) ;
  • Park, Jong-Cheol (Korea Electronics Technology Institute, Korea) ;
  • Lee, Hwack-Joo (New Materials Evaluation Center, Korea Research Institute of Standards and Science)
  • Published : 2004.07.05
Download PDF
⟨ Previous Next ⟩

Abstract

[ $Ba(Zn_{1/3}Nb_{2/3})O_3$ ] (BZN) 세라믹스의 소결 온도는 약 $1350^{\circ}C$ 이다. 그러나 $B_2O_3$가 첨가된 경우, BZN 세라믹스는 $900^{\circ}C$에서 소결되었다. $BaB_4O_7$, $BaB_2O_4$ 그리고 $BaNb_2O_6$ 이차상이 $B_2O_3$가 첨가된 BZN 세라믹스에서 관찰되었다. $BaB_4O_7$과 $BaB_2O_4$ 이차상은 약 $900^{\circ}C$에서 공정 온도를 가지기 때문에 $B_2O_3$를 첨가한 BZN 세라믹스론 $900^{\circ}C$에서 소결하는 동안 액상으로 존재할 것으로 여겨지며, 그것이 BZN 세라믹스의 소결온도를 낮출 것으로 생각된다. 소결 온도의 증가에 따라 유전 상수 ($\varepsilon_r$)와 품질 계수 ($Q{\times}f$)의 값은 증가하였는데, 이는 밀도의 증가에 기인한다. 그러나 $B_2O_3$의 첨가량이 많은 경우 Q 값은 감소하는데, 이는 이차상의 존재가 품질계수의 저하를 초래한다고 생각된다. 2.0 mol% $B_2O_3$가 첨가된 BZN 세라믹스를 $950^{\circ}C$에서 2시간 동안 소결하는 경우, $Q{\times}f$=13.600 GHz, $\varepsilon_r$=37.6 그리고 공진 주파수 온도계수 ($\tau_f$) = 19 ppm/$^{\circ}C$의 유전특성을 얻을 수 있었다.