Low-Temperature Sintering and Microwave Dielectric Properties of the $B_2O_3-$ and CuO-added $Ba(Mg_{1/3}Nb_{2/3})O_3$ Ceramics

$B_2O_3$ 와 CuO가 첨가된 $Ba(Mg_{1/3}Nb_{2/3})O_3$ 세라믹스의 저온소결과 마이크로파 유전특성 연구

[ $B_2O_3$ ] added $Ba(Mg_{1/3}Nb_{2/3})O_3$ (BBMN) ceramics were not sintered below $900^{\circ}C$. However, when CuO was added to the BBMN ceramic, it was sintered even at $850^{\circ}C$. The amount of the $Ba_2B_2O_5$ second phase decreased with the addition of CuO. Therefore, the CuO additive is considered to react with the $B_2O_3$ inhibiting the reaction between $B_2O_3$ and BaO. Moreover, it is suggested that the solid solution of CuO and $B_2O_3$ might be responsible for the decrease of the sintering temperature of the specimens. A dense microstructure without pores was developed with the addition of a small amount of CuO. However, a porous microstructure with large pores was formed when a large amount of CuO was added. The bulk density the dielectric constant $({\varepsilon}_r)$ and the Q-value increased with the addition of CuO but they decreased when a large amount of CuO was added. The variations of those properties are closely related to the variation of the microstructure. The excellent microwave dielectric properties of Qxf=21500 GHz, ${\varepsilon}_r=31$ and temperature coefficient of resonance frequency$({\tau}_f)=21.3\;ppm/^{\circ}C$ were obtained for the $Ba(Mg_{1/3}Nb_{2/3})O_3+2.0\;mol%B_2O_3+10.0$ mol%CuO ceramic sintered at $875^{\circ}C$ for 2h.