Impact Properties of New 3D Composites by Fiber Placement Processing

섬유 자동 배열에 의한 시로운 3D 복합재의 충격특성

In order to improve the damage tolerance of the conventional laminated composites, three­dimensional fiber structures incorporated with stitching yams have been utilized in this study. From the newly developed process termed as TAPIS(TApe Placement Incorporated with Stitching), carbon/epoxy composites have been fabricated. Two-dimensional composites with the same stacking sequence as 3D counterparts have also been fabricated for the property comparison. To examine the damage resistance performance the low speed drop weight impact test has been adopted. For the assessment of damage after the impact loading, specimens were subjected to C-scan nondestructive inspection compression after impact(CAI) were also conducted to evaluate residual compressive strength. Although the damage area of 3D composites was greatly reduced$(30-40\%)$ compared with that of 2D composites, the CAI strength did not show drastic improvement.