EVA, EEA, EBA와 카본블랙 복합재료의 인장강도 및 파단구조 측정

Strain-Stress and Fractural Structure Measurement of EVA, EEA and EBA/Carbon Black Composites

To measure the mechanical and structural properties of semiconducting materials in power cable, we have investigated the stress-strain and fractural structure of semiconducting materials showed by changing the content of carbon black. Those were made as sheets after pressing for 20 minutes at $180[^{\circ}C]$ with a pressure of $200[kg/cm^2]$. The contents of conductive carbon black were 20, 30 and 40(wt%), respectively. The stress-strain experiment was measured by TENSOMETER 2000. The SEM experiment was measured by JSM-6400. From above experimental result, Strain was decreased, while stress was increased according to increment of carbon black content. EEA among resins was best the dispersion of carbon back in base resin from SEM measurement.