Fabrication of Bi2212/Ag HTS Wire with Various Ag Raio

다양한 은비의 Bi2212/Ag 고온초전도 선재의 제조

  • 김상철 (넥상스코리아(주) 기술연구소) ;
  • 하동우 (한국전기연구원 초전도재료연구그룹) ;
  • 오상수 (한국전기연구원 초전도재료연구그룹) ;
  • 오재근 (한국전기연구원 초전도재료연구그룹) ;
  • 송규정 (한국전기연구원 초전도재료연구그룹) ;
  • 하홍수 (한국전기연구원 초전도재료연구그룹) ;
  • 손호상 (경북대학교 금속공학과)
  • Published : 2005.11.10
Download PDF
⟨ Previous Next ⟩

Abstract

Round shape Bi2212/Ag is isotropic and can be fabricated Rutherford cable to transport high current. Bi2212/Ag round wires with various Ag ratio were fabricated using powder-in-tube process. Double stacked 385 (55\times$7) filamentary wire of various wire diameter was heat-treated at various melting temperature. Wires which have Ag ratio of 0.3 and 0.42 of Ag tube for monofilament show similar critical current density. As average filament diameter decreases from 33 to 16 \mu$m, critical current density of wires increase, and in case of 16 ${\mu}m$ and $T_m$ 890$^{\circ}C$, critical current density was 2,062 $A/mm^2$ at 4.2 K, 0 T.