Preparation of dense $BaMgAl_{10}O_{17}:Eu^{2+}$ particles and their surface treatment

Dense $BaMgAl_{10}O_{17}:Eu^{2+}$ phosphor particles with a spherical shape have been synthesized through spray pyrolysis method using basic aluminum nitrate precursor as a spray solution. This $BaMgAl_{10}O_{17}:Eu^{2+}$ particles prepared by the spray pyrolysis have shown the stronger emission intensity compared to the commercially-available $BaMgAl_{10}O_{17}:Eu^{2+}$. However, thermal stability of the BAM:Eu b lue phosphor is very poor due to changing from $Eu^{2+}$ to $Eu^{3+}$ at the thermal process, so brightness of the phosphor decreases. To improve the thermal stability of the dense BAM:Eu phosphor, the spherical BAM:Eu particles were coated with pure $BaMgAl_{10}O_{17}$ layer using the hydrolysis reaction in a solution system. The synthesized powders were characterized by XRD, SEM and PL. On the other hand, the emission properties of the BAM:Eu phosphors coated with $BaMgAl_{10}O_{17}$ layer before and after thermal treatment at $500^{\circ}C$ for 30 min were estimated under VUV excitation. The brightness of the coated phosphor was higher than that of the uncoated phosphor. Also, the coating thickness of BAM layer in the BAM:Eu particles was optimized.