Solution 코팅에 따른 Pb(Zr,Ti)$O_3$ 후막의 강유전 특성

Ferroelectric Properties of Pb(Zr,Ti)$O_3$ Thick Films with Solution Coatings

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the Pb($Zr_xTi_{1-x}$)$O_3$(PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were PZT(70/30) and PZT(30/70), respectively. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 15M, 6-time coated showed the 698. The remanent polarization of the 1.5M, 6-time coated PZT thick films was 38.3 ${\mu}C/cm^2$.