Pore properties and Microstructure on the each regions of a Light-Weight Aggregate using Glass Abrasive Sludge

유리연마슬러지를 사용한 경량골재의 미세구조 및 기공 특성

A light-weight aggregate with a surface layer was fabricated using glass abrasive sludge and expanding agents. The glass abrasive sludges were mixed with expanding agents ($Fe_2O_3,\;graphite,\;CaCO_3$) and formed into precursors. These precursors were sintered in the range of $700-900^{\circ}C$ for 20min. The sintered light-weight aggregate had a surface layer with smaller pores and an inner region with larger pores. The surface layer and pores controlled the water absorption ratio and physical properties. As the expanding agent fraction and the sintering temperature increased, the porosity and pore size increased. The light-weight aggregate with $Fe_2O_3$ and graphite as the expanding agents had a low water absorption ratio while the porous material with $CaCO_3$ as the expanding agent had a higher water absorption ratio and more open pores.