Low-temperature sintering and dielectric properties of the (1-x)$BiNbO_4-(x)ZnNb_2O_6$ ceramics

(1-x)$BiNbO_4-(x)ZnNb_2O_6$ 세라믹스의 저온 소결 및 유전 특성

In this study, the microwave dielectric property variations of (1-x)$BiNbO_4-(x)ZnNb_2O_6$ composites (x=0.3, 0.5 and 0.7) with 10wt% zinc borosilicate(ZBS) glass was investigated as a function of the substitution of $ZnNb_2O_6$ with a view to applying thes system to LTCC technology. The all composition addition of 10wt% ZBS glass ensured a successful sintering below $900^{\circ}C$. In addition, a small amount of $Bi_2SiO_5$ as the secondary phase was observed in the all composition. The substitution of $ZnNb_2O_6$ on the $BiNbO_4$ composites increased the $Q{\times}f$ values, but it decreased the sinterability and dielectric constant due to the high sintering temperature and low dielectric constant of $ZnNb_2O_6\;than\;BiNbO_4$ ceramics. The increasing of $ZnNb_2O_6$ content from 0.3 to 0.7 in the (1-x)$BiNbO_4-(x)ZnNb_2O_6$ composites with 10wt% ZBS glass sintered at $900^{\circ}C$ demonstrated 28.1~15.6 in the dielectric constant$({\varepsilon}_r)$, 5,500~8,700GHz in the $Q{\times}f$ value.