Electrical Properties of V-I Curve of p-ZnO:Al/n-ZnO:Al Junction Fabricate by RF Magnetron Sputtering

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ by RF magnetron sputtering. Target was ZnO ceramic mixed with 2wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}\;to\;4.04{\times}10^{18}cm^{-3}$, mobilities from 0.194 to $2.3cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4{\Omega}cm$. P-type sample has density of $5.40cm^{-3}$ which is smaller than theoretically calculated value of $5.67cm^{-3}$. XPS spectra show that O1s has O-O and Zn-O structures and A12p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.