Low Temperature sintering of $Al_2O_3-TiO_2$ ceramics

저온소결 $Al_2O_3-TiO_2$ 세라믹의 마이크로파 유전특성에 관한 연구

$Al_2O_3-TiO_2$(AT)ceramics shows great promise as a dielectric material for millimeter-wave use. The sintering temperature of AT ceramics was approximately $1450^{\circ}C$ and decreased to $900^{\circ}C$ with the addition of BaCu(B2O5) (BCB) ceramic powder. The presence, of the liquid phase was responsible for the decrease of the sintering temperature. The liquid phase is considered to have a composition similar to the BaO-deficient BCB. The Q-value initially increased with the addition of BCB, but decreased considerably when a large amount of BCB was added, because of the presence of the liquid phase. Good microwave dielectric properties of $Q{\times}f\;=\;16,200\;GHz$, ${\varepsilon}_r\;=\;9$ and ${\tau}_f\;=\;-4\;ppm/^{\circ}C$ were obtained for the 20.0 mol% BCB-added AT ceramics sintered at $900^{\circ}C$ for 2 h.