Synthesis and dielectric properties of the $ZnAl_2O_4$ ceramics for low-firing

저온소결용 $ZnAl_2O_4$ 세라믹스의 합성 및 유전 특성

Synthesis and dielectric properties of glass-ceramic composites with zinc borosilicate glass(here after ZBS glass) were investigated as functions of $ZnAl_2O_4$ phase synthesis method, glass addition (50~60 vol%) and sintering temperature ($600{\sim}950^{\circ}C$ for 2 hrs). The 50 vol% ZBS glass-$Al_2O_3$ and 60 vol% ZBS glass-$ZnAl_2O_4$ ensured successful sintering below $900^{\circ}C$. But the composition of 100-x-y vol% ZBS glass-x vol% $Al_2O_3-y$ vol% ZnO exhibited poor sinterability below $900^{\circ}C$ and the swelling phenomenon occurred in this composite with the large amount of ZBS glass. The sintering behavior of Glass-ceramic composites was affected by the crystallization of $ZnAl_2O_4$ which was formed by the reaction between ZBS glass and $Al_2O_3$. Dielectric constant (${\varepsilon}_r$), $Q{\times}f$ value and temperature coefficient of resonant frequency (${\tau}_f$) of the composite with 50 and 60 vol% ZBS glass contents demonstrated $ZBS-Al_2O_3({\varepsilon}_r=5.7)$, $ZBS-ZnAl_2O_4({\varepsilon}_r=5.8)$ which is applicable to substrate requiring an low dielectric properties.