The Experimental Study on the Plaster mortar using Recycled fine aggregate

순환잔골재를 사용한 미장용 모르타르에 관한 실험적 연구

The use of the recycled fine aggregate to the material of structural concrete is not easy currently because there are some problems, such as the difficulty of quality control and the badness of chemical and physical property other than river sand, crushed fine aggregate. To use of recycled fine aggregate, many researches on the recycling of recycled fine aggregate have been studying until today. However, the result of the research is little except for some results. Therefore, the purpose of this study is to confirm the possibility of use of recycled fine aggregate for raw material of plaster mortar. In this study, various tests were performed such as flow, air content, unit weight, bond strength, and compressive strength test to evaluate the effect according to the substitution of recycled concrete aggregate. The results of strength test showed that the concrete strength improved with the increase of replacement ratio of recycled fine aggregate. In the other side, flow and air content are decreased according to replacement ratio of recycled fine aggregate. The result of this study could be used as the basic data for the recycling of recycled fine aggregate.

순환잔골재를 구조체용 콘크리트의 잔골재로 이용하는 것은 아직까지 품질관리 및 불확실한 내구성 등으로 활성화가 어려운 실정이다. 따라서 구조체용 보다는 2차제품 분야에서의 순환잔골재의 재활용성을 기대해 볼 수 있는데, 특히 미장용 모르터의 경우, 입도 및 흡수율 등의 요구성능을 만족한다면 일반 잔골재의 대체재로써 순환잔골재를 사용 가능할 것으로 판단된다. 이에 본 연구에서는 미장용 모르터의 일반 잔골재를 순환잔골재의 대체율에 따른 특성을 검토하기위해, 플로우, 공기량, 단위용적중량, 부착강도, 압축강도 실험을 실시하였다. 실험결과, 순환골재 대체율에 따른 플로우 및 공기량은 감소하는 결과를 보였으며, 단위용적중량 및 압축강도는 순환골재 대체율이 증가함에 따라 각각 단위용 적중량과 압축강도가 증가하는 결과를 나타냈다. 따라서 본 실험결과 순환잔골재를 미장용 모르터의 일반잔골재 대체재로써 적용이 가능한 것으로 나타났다.