Mechanical Properties of Recycled Powder mixing Concrete

재생미분말을 혼입한 콘크리트의 역학적 특성

The problem of disposing construction waste materials has become a national and social problem. Recycled powder generated in the process of making aggregate, and the recycled powder is land-filled in its entirety. Results of toxicity testing of recycled power show that it contains base-pair substituent mutagenicity. As recycled powder is disposed of as landfill, it can cause secondary contamination such as soil and underground water contamination. There has been very little research made on recycled powder. This study has examined the utilization of concrete mixture by using recycled powder in a mixture instead of cement and compared and analyzed the characteristics of dynamics and workability. This study has examined the application of recycled powder in concrete. Depending on the replacement rate and workability, test piece was manufactured using different mixing rate by CP, WCP, PCP. The CP was used to examine the physical property of concrete and characteristics its dynamics. The letters W of WCP and P of PCP are the initials of water and mixture. They were made using the standard mixing ratiosemphasizing the workability to determine the characteristic of dynamics of concrete based on the mixing ratio of recycled powder. With the increase in the replacement rate, CP had very little change in the strength. But with the decline of slump, the workability was not good. The result of manufacturing WCP and PCP using the standard mixing ratio showed that WCP had a drop in strength compared to the plain. PCP had almost the same value as the plain only when the replacement rate was 10%. When it was higher than that, a reduction in strength was observed.

건설폐기물의 처리문제는 국가 사회적 문제로 제기되고 있으며 순환골재의 생산과정에서 발생하는 재생미분말은 전량 폐기 매립되고 있다. 재생미분말의 독성 시험결과 염기치환형 돌연변이원성을 포함하고 있다. 이와 같이 독성을 갖는 재생미분말이 매립 처분됨으로서 토양 및 지하수 오염등 2차 오염을 초래할 수 있다. 그러나 재생미분말을 재활용에 대한 연구가 매우 미흡한 실정이다. 본 연구에서는 재생미분말을 재활용하기 위한 방법으로 콘크리트의 혼화제를 활용하고자 시멘트 대신 재생미분말을 혼입하여 역학적 특성과 작업성을 비교 분석하였다. 실험은 CP, WCP, PCP로 배합비를 달리하여 공시체를 제작하여 실험을 실시하였다. CP은 재생미분말 혼입율에 따른 콘크리트 물리적 성질과 역학적 특성을 파악하고자 하였으며, WCP의 W자와 PCP의 P자는 각각 물과 혼화제의 이니셜로 슬럼프, 공기량을 표준배합에 맞게 제작하여 워커빌리티에 중점을 두고 재생미분말 혼입률에 따른 콘크리트의 역학적 특성을 보고자 하였다. CP는 치환율의 증가에 따라 강도 변화는 거의 일어나지 않았지만 슬럼프의 저하로 인해 워커빌리티가 좋지 않았다. WCP, PCP는 표준배합에 맞게 제작을 하여 실험한 결과 Plain에 비해 WCP는 강도저하가 일어났으며, PCP는 치환율이 10%일 때만 Plain과 거의 같은 값을 가지고 그 이상일 때는 강도저하가 일어났다.