Fabrications and Properties of Al/$VF_2$/$n^+$-Si(100) Structures by Dip Coating Methode

Dip Coating 법에 의한 Al/$VF_2$-TrFE/Si(100) 구조의 제작 특성

Ferroelectric vinylidene fluoride-trifluoroethylene ($VF_2$-TrFE) copolymer films were directly deposited on degenerated Si ($n^+$, 0.002 $\Omega{\cdot}cm$) using by dip coating method. A 1 ~ 3 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene ($VF_2$:TrFE=70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers using dip coating method for 10 seconds. After Post-Annealing in a vacuum ambient at 100~200 $^{\circ}C$ for 60 min, upper aluminum electrodes were deposited by thermal evaporation through the shadow mask to complete the MFS structure. The ferroelectric $\beta$-phase peak of films, depending on the annealing temperature, started to show up around $125^{\circ}C$, and the intensity of the peak increased with increasing annealing temperature. Above $175^{\circ}C$, the peak started to decrease. The C-V characteristics were measured using a Precision LCR meter (HP 4284A) with frequency of 1MHz and a signal amplitude of 20 mV. The leakage-current versus electric-field characteristics was measured by mean of a pA meter/DC voltage source (HP 4140B).