Al 이온 주입된 p-type 4H-SiC에 형성된 Ni/Ti/Al ohmic contact의 특성

Characteristics of Ni/Ti/Al ohmic contact on Al-implanted 4H-SiC

Ni/Ti/Al multilayer system was tested for low-resistance ohmic contact formation to Al-implanted p-type 4H-SiC. Compared with conventional process using Ni, Ni/Ti/Al contact shows perfect ohmic behavior, and possesses much lower contact resistance of about $2.5\times10^{-4}\Omega{\cdot}cm^2$ after $930^{\circ}C$ RTA, which is about 2 orders of magnitude smaller than that of Ni contact. Contact resistance gradually increased as the RTA temperature was lowered in the range of 840 ~ $930^{\circ}C$, and about $3.4\times10^{-4}\Omega{\cdot}cm^2$ was obtained at the lowest RTA temperature of $840^{\circ}C$. Therefore, it was shown that RTA temperature for ohmic contact formation can be lowered to at least $840^{\circ}C$ without significant compromise of contact resistance.