Abstract
In this work, an air-bending test using magnesium alloy ZK60 sheet was carried out at the various temperatures from room temperature to $300^{\circ}C$ in order to investigate the effect of grain size on the spring-back characteristic. It was found out from experiments that the amount of spring-back was nearly zero at all temperature range when the specimens with grain sizes of 14.66 and $60.71{\mu}m$ were bent by $90^{\circ}$. On the other hand, the spring-back amount dramatically increased at room temperature and phenomenon of spring-go was observed at high temperature when the specimen with submicro grain size of $0.98{\mu}m$ was bent by $90^{\circ}$. From this kind of different spring-back characteristics according to the grain size, it was confirmed that the grain size of material is one of the important factors which have an effect on the spring-back.