Sintering and Microwave Properties of Ba Hexagonal Ferrite

Ba 육방정 페라이트의 소결 특성 및 마이크로파 특성

The sintering and high frequency electro-magnetic properties of Ba-hexagonal ferrite were investigated. All samples of the Ba-hexagonal ferrite were prepared by the conventional mixed oxide method and sintered at $1150^{\circ}C$~$1400^{\circ}C$. From the X-ray diffraction patterns of sintered Ba-hexagonal ferrite, the $Ba_3Co_2Fe_{24}O_{41}$ phase was represented as main phase in the almost sintering conditions. The bulk densities with sintering temperature and decreased at $1400^{\circ}C$. The permittivity ($\varepsilon$') and loss tangent of permittivity ($\varepsilon$"/$\varepsilon$') of $Ba_3Co_2Fe_{24}O_{41}$ ceramics increased and decreased with sintering temperature, respectively. The permeability of $Ba_3Co_2Fe_{24}O_{41}$ ceramics decreased with sinteirng temperature. The loss tangent of permeability was not changed compared each other with sintering temperature. The bulk density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics sintered at $1300^{\circ}C$ was 4.79 g/$cm^3$. The permittivity, loss tangent of permittivity and permeability, loss tangent of permeability were 19.896, 0.1718 and 14.218, 0.2046 at 210 MHz, respectively.