The study of ethanol electro-oxidation using ternary electrocatalysts

삼원소 전극촉매 이용에 따른 에탄올 산화반응에 관한 연구

PtRu based and PtSn based ternary catalysts were prepared by a conventional impregnation method using NaBH4 as reducing agent. The alloy formation, crystalline size and chemical composition of the in-house catalysts were determined by XRD, TEM and EDX, respectively. The chemical compositions of in-house catalysts were quite similar to the nominal value and good alloy formations were also observed. Further, crystalline sizes of ternary catalysts were comparatively smaller than binary catalysts and were approximately 3.5 ~ 5.5 nm. The electrochemical measurements were carried out in the solution 1 M $H_2SO_4$ with 1 M $C_2H_5OH$ at room temperature. LSV results obtained that ternary catalysts were higher current densities and specific activities. Especially, in case of tungsten addition system, Pt5Sn4W/C have the highest specific activities values and was approximately 21.2 and 3.1 times higher than that of PtRu/C and PtSn/C electrocatalyst.