Chalcopyrite semiconductor $CuInSe_2$ nanoparticles were prepared using a low temperature colloidal route by reacting the starting materials (CuI, $InI_3$ and $Na_2Se$) in solvents. After synthesised $CuInSe_2$ nanoparticles precursors were mixed with organic binder for the viscosity of the precursor slurry to be suitable for the doctor blade method. The mixture of $CuInSe_2$ and binder was deposited onto molybdenum-coated sodalime glass substrates to form thin film. The precursor thin films were preheated on the hot plate to remove remaining solvents and binder material. After subsequent thermal processing of the thin film under a selenium ambient, $CuInSe_2$ absorber layer with grain size significantly lager than that of the nanoparticles was formed.