Abstract
A non-vacuum process for fabrication of $CuIn_xGa_{1-x}Se_2$ (CIGS) absorber layer from the corresponing Cu, In, Ga solution precursors was described. Cu, In, Ga precursor solution was prepared by a room temperature colloidal route by reacting the starting materials $Cu(NO_3)_2$, $InCl_3$, $Ga(NO_3)$ and methanol. The Cu, In, Ga precursor solution was mixed with ethylcellulose as organic binder material for the rheology of the mixture to be adjusted for the doctor blade method. After depositing the mixture of Cu, In, Ga solution with binder on Mo/glass substrate, the samples were preheated on the hot plate in air to evaporate remaining solvents and to burn the organic binder material. Subsequently, the resultant CIG/Mo/glass sample was selenized in Se evaporation in order to get a solar cell applicable dense CIGS absorber layer. The CIGS absorber layer selenized at $530^{\circ}C$ substrate temperature for 1h with various metal organic ratio.