Characterization of effects of cadmium selenide on the performance of poly(3-hexylthiophehe):[6,6]-phenyl $C_{61}$ butyric acid methyl ester organic solar cells

Cadmium selenide 영향에 따른 poly(3-hexylthiophehe):[6,6]-phenyl $C_{61}$ butyric acid methyl ester 유기태양전지 특성 분석

  • Published : 2011.11.16

Abstract

We studied the performance of CdSe nanoparticle in the active layer of organic photovoltaics (OPVs) by changing concentration of the CdSe NPs in the P3HT:PCBM layer. We observed that the absorption peak value gradually increases with the increasing amount of CdSe NPs at 600nm wave length. However, the electrical properties of OPVs correspond less with the tendency of UV/visible result. The highest performance was shown with 10% of CdSe NPs. The device performance decreased after 10% of CdSe NPs, this shows the dependencies of performanc of hybrid solar cells on the CdSe NPs loading amount. The resulting OPVs with 10 % of CdSe NPs show a short circuit current density ($J_{sc}$) of $6.96mA/cm^2$, open circuit voltage ($V_{oc}$) of 0.61V, fill factor (FF) of 0.59, and power conversion efficiency (PCE) of 2.53% under AM 1.5 ($100mW/cm^2$).

Keywords