Effect of $CaSO_4$ and $BaSO_4$ on the Formation of Portland Cement Clinker

Portland Cement Clinker 생성반응에 미치는 $CaSO_4$ 및 $BaSO_4$의 영향

  • 서일영 (한양대학교 요업공학과) ;
  • 최상흘 (한양대학교 요업공학과)
  • Published : 1974.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Effect of calcium sulfate and barium sulfate on the formation of portland cement clinker was studied by means of chemical analysis. DTA and X-ray diffraction analysis. In the presence of liquid phase, effect of the additives on the formation of tricalcium silicate was examined according to the reaction, 2CaO.$SiO_3$＋CaO$\longrightarrow$3CaO.$SiO_3$, which is the principal reaction in portland cement clinkerization, and optimum conditions in firing clinker concerning amount of additive, firing time and temperature were determined, and its kinetics was referred to. The experimental results are summerized as follow: (1) Appropriate burning temperature range of cement clinker is more limited as the content of calcium sulfate in clinker is increased. Amount of calcium sulfate, firing time and temperature in proper condition of clinkerization is related to each others. Being added suitable quantity of calcium sulfate, firing temperature of clinker can be lowered about $100^{\circ}C$. (2) When 3-5 mole% of calcium sulfate is added, firing time of 15-30 minutes at about $1380^{\circ}C$ is reasonable, and if the content is over7 mole %, firing for 1 hr. or more at $1350^{\circ}C$ is anticipated to be optimum condition. (3) In the reaction of tricalcium silicate formation, the role of barium sulfate as a mineralizer is similar to that of calcium sulfate, but the optimum firing temperature of cement clinker containing barium sulfate tends to be 20-$30^{\circ}C$ higher than that of clinker containing calcium sulfate. (4) When barium sulfate is used as mineralizer, 2-3 mole % of it to tricalcium silicate is recommended and if it is added more than this amount, free CaO is increased rapidly in clinker and alite formation is inhibited.

Keywords

References

  1. The 5th I.S.C.C. v.1 Mechanism and Kinetics of Portland Cement Clinker Formation in the Presence of Liquid Phase R. Kondo;S. H. Choi
  2. J. Am. Ceram. Soc. v.53 no.7 Diffusion in Portland Cement Clinker N.H. Christensen;K.H. Simousen
  3. Cement-Wapno-Gips v.16 no.26 Influence of P₂O₃ on the Mineral Structure of Protland Cement M. Musialik;A. Gruszezynska
  4. Tr. Gos. Vses. Inst. po Proektir. i Nauchn-Issled. Robotam v Tsementn. Prom. no.20 Composition and Characteristics of the Crystallization of 3CaO·SiO₂ in the Presence of Admixtures A.P. Khashkovskaya;M.M. Sychev;V.I. Korneev
  5. The 4th I.S.C.C. v.1 Effects of the Minor Components on the Hydraulicity of the Calcium Silicates J.H. Welch;W. Gutt
  6. J. Appl. Chem. v.2 Effect of Phosphate on the Constitution and Hardening of Portland Cement R.W. Nurse
  7. The 5th I.S.C.C. v.1 Problem of Admixtures M.M. Sichov
  8. Silikaty v.9 no.1 Decomposition of Tricalcium Silicate with Boron Oxide S. Mircea
  9. Tr. Gos. Vses. Inst. po Proektir. i Nauchn-Issled. Robotam v Tsementn. Prom. no.28 Effect of Admixtures of Raw Materials and Alloying Additions on the Solid Phase Reaction in the CaO-SiO₂ System M.M. Sychev;V.I. Korneev;L.M. Karpova
  10. Dokl. Akad. Nauk SSSR v.109 The Problem of the Stabilization of Ca₂SiO₄ G.V. Kukolev;M.T. Melnik
  11. セメント技術年報 v.17 ポルトランドセメントクリカ-①鑛物組成におよぽす特殊成分の影響 近藤連一
  12. Trudy Khar'Kov. Polilekh. Inst. v.17 Influence of Cr₂O₃, $P_2O_5$, $V_2O_5$ and BaO on the Hardness and the Crushability of Portland Cement Clinker M.T. Meknik
  13. Tr. Mosk. Khim.-Tekhn. Inst. no.45 Study of Properties of Minerals and Cements Containing CdO and TrO₂ M.R. Raman Kulov;Yu. M. Butt;V.V. Timashev
  14. The 5th I.S.C.C. v.1 Miscibilities of Special Elements in Tricalcium Silicate and Alite, and the Hydration Propertes of Tricalcium Silicate Solid Solutions R. Kondo;K. Yoshida
  15. The 5th I.S.C.C. v.1 The Effect of Minor Components on the Early Hydraulic Acrivity of the Major Phases of Portland Cement Clinker T. Sakura;T. Sato;A. Yoshinaga
  16. Chimica v.13 The Chromium Content of Cement R. Flatt
  17. Silikattech. v.11 Reaction Kinetics of the System CaO-SiO₂ in Presence of Catalysts A. Bereczky
  18. The 5th I.S.C.C. v.1 New Compound $Ca_{12}Si_4O_{19}F_2$ in the System CaO-SiO₃-CaF₂and the Role of CaF₂in the Burning of Cement Clinker M. Tanaka;G. Sudoh;S. Akaiwa
  19. 窯業會誌 v.6 no.1 Cement Clinker 燒成에서 CaF₂의 Mineralizer 效果와 Cement 物性에 미치는 影響 金鎭元
  20. セメント技術年報 v.16 ポルトランドセメント製造原料にカルシウムサルフエイトを添加したセメントに關する硏究 福田廷衛
  21. Zhur. Priklad Khim. v.35 Effect of Gypsum on Mineral Formation in Cement Clinker P.P. Budnikov;I.P. Kuznetsova
  22. セメント技術年報(日) v.26 原料に石てらを添加して燒成したクリニカの强度發現性について 赤津建;池田五十六
  23. Tr. Gos. Vses. Nauch-Issled. Inst. Tsementn. Prom. no.23 Barium Containaing Portland Cement I.V. Kravchenko;O. K. Aleshma;L.N. Grikevich
  24. Pol. Akad. Nank, Oddzial Krakowie, Pr. Kom. Ceram. no.18 Effect of Additions of Barium on Properties of Portland Cement Clinker W. Kurdowski
  25. Zement-Kalk-Gips v.13 no.3 Refractory Alumina Cement containing Barium Oxide A. Braniski;T. Lonesov
  26. Cement-Wapno-Gips v.26 no.9 Rapid-setting Barium Aluminate-based Cements B. Rozanowski;M. Knabel;M. Handke
  27. Silikat Techn. v.12 Effect of BaO on Clinkerization. Ⅱ, Effect of BaO and MgO on the Viscosity of the Liquid Phase I.I. Kholin;Yu. S. Malinin;S.B. Entin
  28. 窯業協會誌(日) v.78 no.3 クリンカ-融液へのクリンカ-成分鑛物の溶解 崔相紇;近藤連ソ
  29. Tsement v.32 no.4 Effect of Admixtures of Raw Materials and Alloying Additions on the Viscosity of Liquid Phase in Portland Cement M.M. Sychev;P.B. Zozulya;M. Stefan;S.M. Ivanetsova
  30. Dokl. Akad. Nauk SSSR v.144 Diffusion Coefficient of calcium in the Liquid Phase During the Calcination of the Portland Cement Clinker P.P. Bundikov;E.E. IIolin;S.B. Entin
  31. 漢陽大論文集 v.3 Portland Cement Clinker 生成反應에 關한 硏究 崔相紇
  32. J. Am. Ceram. Soc. v.49 no.7 Numerical Data for some Commonly Used Solid State Reaction Equations J.H. Sharp;G.W. Brindley;B.N. Narahaiachar