Utilization of Alunite to Ceramic Raw Materials (III)

요업원료로서 명반석의 이용에 관한 연구(제III보) Mullite질내화재원료로의 이용

  • 백용혁 (전남대학교 요업공학과) ;
  • 최상흘 (한양대학교 요업공학과)
  • Published : 1974.09.01

Abstract

The possibility of the sources for the manufacture of mullite-rich refractories from the modified domestic alunite was studied. The modifying method of alunite studied were performed by calcination, wet ballmilling, and washing with water. For synthesis of mullite-rich refractories, the modified alunite with the addition of alumina and Fe2O3 as mineralizer was fired at 1350$^{\circ}$-155$0^{\circ}C$, and the following results were obtained: 1) The suitable firing temperature range was 1450$^{\circ}$-150$0^{\circ}C$, and adequate amounts of Al2O3 and Fe2O3 were below 30% and 3~4%, respectively. 2) Thermal expansion coefficient proportional to heating temperature was about 5$\times$10-6~10$\times$10-6cm/cm.deg. 3) The mineralogical compositions of the sintered specimens were found as mainly mullite and corundum.

Keywords

References

  1. 窯業會誌 v.9 no.3 窯業源料로서明礬石의 利用에 관한 硏究 (Ⅰ) 崔相紇;白龍赫;朴哲元
  2. 窯業會誌 v.10 no.2 窯業源料로서明礬石의 利用에 관한 硏究 (Ⅱ) 崔相紇;朴哲元;徐一榮;白龍赫
  3. J. Am. Ceram. Soc. v.36 Effect of $TiO_2,\;Fe_2O_3$ and Alkali on Mineralogical and Physical Properties of Mullite Type and Mullite Forming $Al_2O_3-SiO_2$ Mixtures K.G. Skinaer;W.II.Cook;R.A.Potter;H.PalmourⅢ
  4. 요업회지 v.10 no.2 몰라이트 합성에 관한 기초적 연구 이종근;한상목;조항근;김칠영
  5. Ogneupory;日寫協誌 v.33;77 no.12;84 高알루미나 耐火物의 相組成變化 S.P. Smitt-Fogelovic
  6. 窯業會誌 v.6 no.2 Mullite質耐火匣製造에 關한 硏究 池應業;梁之鉉;池亨健
  7. 窯業學會誌 v.11 no.1 高알루미나質原料로서 漣川産 紅柱石의 利用에 關한 硏究 安永弼;최롱
  8. J Am. Ceram. Soc. v.41 Subsolidus Relations between Mullite and Iron Oxide W.E. Brownell
  9. Amer. Ceram. Soc. Bull. v.53 Influence of Mineralizers on the Constitution of Hard Porcelain S.P. Chaudhuri
  10. Trans. Brit Ceram. Soc. v.44;45;49 The Refractory Properties of Alunite J.O. Knizek;H. Futter
  11. 日窯協誌 v.74 no.5 明礬石의 諸性質과 窯業原料로서의 利用에 關한 硏究 素木洋一;鈴木早惠子