Abstract
This study was conducted to research the formation, color development and application for colored glazes of the spinel solid solutions of the green pigment. On specimens prepared by calcining the oxide and basic carbonate mixture at 1250℃ for 1.5 hour, the x-ray analysis, measurement of reflectance and the test of their stabiality as a glaze pigment were carried out. The results are summarized as follows 1) Each sample is composed of single spinel and not of mixture of spinel. 2) Formation of continuous soild solution, except for a few instances, pertaining to Vegard's law was confirmed by means of the x-ray analysis. 3) The more difference between absorption and reflectance lies, the lighter colors are. When the absorption occurs at the high-reflectance, the excitation purity becomes low. On the contrary when the absorption takes place at the low-reflectance, the excitation purity becomes low. On the contrary when the absorption takes place at the low-reflectance, the excitation purity is higher. 4) Colors obtained in the CdO-MgO-Cr2O3-Al2O3 system, as the amounts of Al3+ increased, change from green through brown to pink, and the absorption peak shifts towards violet region. 5) An increase in Co2+ in the CoO-MgO-Cr2O3-Al2O3 system, changes the color from blue green to dark blue. The excitation purity is higher, and the absorption peak shifts toward regions. 6) Colors are green in the NiO-MgO-Cr2O3 and CdO-MgO-Cr2O3 systems in general, but in the ZnO-MgO-Cr2O3 system brillant hue is not obtained. 70 According to the results of the colored glaze test, the spinels turn outto be stable as brilliant glaze pigment in the calcium-magnesia glaze.