Applications of Irradiation to Polyethylene for Flame Retarded Wire and Cable Insulation

방사선에 의한 폴리에칠렌의 난연성전선 및 케이블에 관한 연구

The properties of polyethylene materials exhibit good insulation and radiation resistance, but exhibit poor flame resistance. Flame retardant properties of the polyethylene were improved by the radiation induced grafting or crosslinking. When the various flame retardants were fixed onto polyethylene, the amount of fixation in grafting was increased with the increase of radiation dosages. In the case of grafting, it is necessary for high grafting yield that the polyethylene films were swelled before irradiation with ${\gamma}$-rays or electron beams. It is the suitable method for the fixation of flame retardant that polyethylene samples were blended with various flame retardants at 1$25^{\circ}C$ and then blended polymers were crosslinked by the electron beams at room temperature.

고분자피복재 중 polyethylene은 전기적 절연성 및 내방사선성이 좋으나 난연성이 결여되어 있으므로 이 단점을 개질하였다. 방사선을 이용하여 polyethylene에 여러 종류의 난연제를 고착시켰는데 grafting 방법과 blending후 crosslinking 방법을 사용하였다. 일반적으로 grafting시키는 경우 시료에 난연제가 고착되는 량은 방사선선량이 증가할수록 증가하였다. Grafting 방법으로 polyethylene에 난연제를 고착시킬 때 시료를 팽윤(swelling)시켜서 난연제를 grafting시켜야 한다. Blending 한 후 crosslinking시킨 경우 시료와 난연제의 량을 자유롭게 조절하여 blending하여 crosslinking시킬 수 있는 이질이 있다. 난연제를 고착시키는 2가지 방법중 blending후 crosslinking 시키는 방법이 가장 바람직하다.