Studies on the Active Materials of Alkaline Storage Battery. On Cadmium Electrode

알칼리 축전지의 활물질에 관한 연구. 카드뮴 전극에 관하여

  • Ju Seong Lee (Department of Industrial Chemistry, Hanyang University) ;
  • Choong Yeoul Joo (Department of Industrial Chemistry, Hanyang University) ;
  • Park, Su Gil (Department of Industrial Chemistry, Hanyang University)
  • 이주성 (한양대학교 공과대학 공업화학과) ;
  • 주충렬 (한양대학교 공과대학 공업화학과) ;
  • 박수길 (한양대학교 공과대학 공업화학과)
  • Published : 1981.10.30

Abstract

The electrochemical behavior of cadmium electrode for the nickel-cadmium battery system has been studied by cyclic voltammetry, controlled potential electrolysis and X-ray diffraction method. Cathodic polarization curve for cadmium hydroxide electrode prepared by electrochemical pretreatment of metallic cadmium showed two peaks. It has been found that cadmium hydroxide was reduced to cadmium metal at the first peak potential, whereas very activated metal of cadmium which was strongly oriented (002) rather than (101) was formed at the second peak potential. It was also found that the cadmium formed at the second peak potential reacted rapidly with oxygen. Therefore, it could be presumed that the cadmium recombination reaction with the oxygen was chemical, and could be represented as $2Cd + O_2 + 2H_2O\;{\longrightarrow}\;2Cd(OH)_2$.

Ni-Cd 전지 중 카드뮴 전극을 수산화 칼륨용액 중에서 각종 조건의 변화에 따른 cyclic voltammetry를 행하여 카드뮴전극의 전기화학적 거동을 검토하였으며 voltammogram에 나타나는 peak전위 근처의 각 전위에서 정전위 전해를 하여 충, 방전상태의 전기화학적 거동을 X-선 회절선도의 해석 결과와 결부시켜 전극반응 메카니즘을 종합적으로 검토하였다. 수산화카드뮴 마이너스 전극의 음극분극 곡선에는 두 개의 peak가 나타난다. 마이너스극의 수산화카드뮴은 제 1 peak 전위에서 카드뮴 금속으로 환원되고 제 2 peak 전위에 도달하면 매우 활성이 큰 금속 상태로 되며 (002)면이 (101)면보다 성장이 매우 크다. 또한 제 2 peak 전위의 카드뮴은 산소와의 선택적인 반응이 급속히 일어남을 알 수 있었다. 본 실험의 결과 카드뮴극과 산소와의 반응은 화학적 반응인 $2Cd + O_2 + 2H_2O\;{\longrightarrow}\;2Cd(OH)_2$으로 진행된다고 추정하였다.

Keywords

References

  1. J. Electrochem. Soc. v.105 P. E. Lake;E. J. Casey
  2. J. Electrochem. Soc. v.106 P. E. Lake;E. J. Casey
  3. J. Electrochem. Soc. v.106 G. T. Groft
  4. J. Electrochem. Soc. v.107 S. Uno Falk
  5. Elektrotech. v.11 H. Winkler
  6. J. Electrochem. Soc. Japan (Overseas Suppl. Ed.) v.28 T. Hosono;M. Matsui
  7. Denkikagaku v.27 T. Hosono;M. Matsui
  8. Denkikagaku v.28 T. Hosono;M. Matsui
  9. Denkikagaku v.29 T. Hosono;M. Matsui
  10. Denkikagaku v.30 T. Hosono;M. Matsui
  11. Electrochimica Acta v.5 S. Yoshizawa;Z. Takhara
  12. Z. Elektrochem. v.10 R. W. Ohse
  13. Electrochimica Acta v.3 S. Visvanathan;S. Ananthanarayanan
  14. J. Electrochem. Soc. v.116 J. P. Elder;E. M. Jost
  15. Denkikagaku v.38 Z. Takehara;S. Yoshizawa
  16. J. Electroche. Soc. India v.19 R. Krishnan(et al.)
  17. J. Electrochem. Soc. v.124 G. Halpert;L. May
  18. Power. Sources v.6 R. W. Bramham(et al.)
  19. J. Electrochem. Soc. v.109 A. J. Salkind;P. F. Bruins
  20. National Tech. Report(Matsusita Electrical Co.) v.16 S. Oda(et al.)
  21. National Tech. Report(Matsusita Electrical Co.) v.16 K. Kanetsuki(et al.)
  22. Trans. Faraday Soc. v.51 P. Hersch
  23. Proc. 12th Annual Battery Research and Development Conference G. Boars
  24. Proc. 12th Annual Battery Research and Development Conference A. Fleischer