Abstract
The composition of glasses to be suitable for crystallisation of $BaTiO_3$ by heat-treatment and the dielectric properties of the glass-ceramics were investigated. The composition of the family of glasses was defined by the formula $\chi$ $BaTiO_3 + (100-$\chi$)Al_2O_3$.$2SiO_2$ and excess BaO. Data were presented on dielectric constant and loss tangent at various frequencies. The effects of excess BaO on dielectric properties were investigated. The additions of $Na_2O$ and $Nb_2O_5$ shifted the Curite temperature of these glass-ceramics. The glass composition which was able to be melted at 145$0^{\circ}C$ and moulded as homogeneous glass phase without devitrification should contain $Al_2O_3$.$2SiO_2$ more than 30 mole %. The more the amount of additive BaO increased, the more dielectric constant increased. When the maximum heat-treatment temperature was 105$0^{\circ}C$, we obtained higher dielectric constant than that of 95$0^{\circ}C$. The dielectric constant and the dielectric loss were stable at frequencies between 5$\times$104 and 107 cycle per second. When $Na_2O$ and $Nb_2O_5$ were added, the Curie temperature, presented at 14$0^{\circ}C$ to 15$0^{\circ}C$, shifted to lower temperature. Therefore, the glass-ceramics having high dielectric constant at room temperature were obtained.