Abstract
Barium titanate powder was made by firing the complex hydroxide which had been synthesized with chemical wet process by the medium of $H_2O_2$. This experiment was done as following A mixed solution of $BaCl_2$, $TiCl_4$ and $H_2O_2$ with 1:1:10 mol ratio was prepared. Ammonium hydroxide was added into the mixed solution. In the range of pH 8-10 $BaTiO_3$ complex hydroxide was obtained and treated at room temperature 11$0^{\circ}C$, 20$0^{\circ}C$, 40$0^{\circ}C$ and $600^{\circ}C$. The results obtaiined from this experiment were as follows. At room temperature $BaTiO_3$ complex hydroxide was amorphous. Above 10$0^{\circ}C$ crystalline $BaTiO_3$ was obtained and particle size of $BaTiO_3$ was increased with elevated temperature. So the particle size of BaTiO3 could be controlled by the firing temperature. After treating $BaTiO_3$ complex hydroxide at 10$0^{\circ}C$ the average particle size of $BaTiO_3$ was 0.22$\mu\textrm{m}$.