The Effect of Additive Zirconia on Properties in Sintered Body of Chamotte-Kaolin-Agalmatolite System

Chamotte-Kaolin 납석계 소결체의 특성에 미치는 $ZrO_2$의 첨가효과

  • 박금철 (한양대학교 무기재료공학과) ;
  • 이석로 (한양대학교 무기재료공학과)
  • Published : 1984.04.01

Abstract

Unstabilized Zirconia was added to basic composition under 44$mu extrm{m}$ of 57.80wt% Clay-22.20wt% Chamotte-20.00wt% Agalmatolite system. Here the amount and the particle size of Zirconia were 5-25wt% and -20${\mu}{\textrm}{m}$ respectively and the body of these composition was first at 135$0^{\circ}C$. The results obtained from examining the properties of sintered body were as follows. 1. Firing linear shrinkage apparent density and bulk density apparent porosity and water absorption of the samples had the tend to increase according as the particle size of zirconia became larger and the amount of zirconia increased. 2. Modulus of rupture was inversely proportional to the particle size and the additive amount of zirconia, . Especially in case that the particle size of zirconia over 5${\mu}{\textrm}{m}$ and the additive amount of zirconia was 25wt% the modulus of rupture had shrunk drastically. 3. The maximum value of KIC was obtained at 20wt% additive amount of zirconia according to the each particle size of zirconia. Especially the highest value of KIC is 2, 173 M. Pa. M1/2 when the particle size of zirconia is 5~10${\mu}{\textrm}{m}$ and the additive amount is 20wt%.

Keywords

References

  1. M.S. Thesis A Study on the Effect of ZrO₂Additive on the Properties of Sintered Body of 96wt.%Al₂O₃-2wt.%TiO₂System Moon, Bong-Ki
  2. Nature v.258 Ceramic Steel R.C. Garvle;R.H Hannink;R.T Pasco
  3. J. Mat. Sci v.13 Effect of Stress-Induced Phase Transtormation on the Properties of Polycrystalline Zirconia Containing Metastable Tetragonal Phase T.K. Gupta;F.F. Lange;J.H. Bechtold
  4. J. Am . Ceram. Soc v.62 no.5-6 Microstructural Development in MgO-Partially Stabilized Zirconia(Mg-PSZ) D.L. Porter
  5. Ceram. Soc. Bull. Jap. v.17 no.6 高 强度 高じん性 ジハユこフ 小林 啓佑;正木 孝樹
  6. Am. Ceram. Soc. Bull. v.56 no.6 Effect of Induced Microcracking on the Fracture Toughncss of Ceramics N. Claussen
  7. J. Am. Ceram. Soc v.59 no.1-2 Fracture Toughness of Al₂O₃with an Unstabilized ZrO₂Dispersed Phase N Claussen
  8. J. Am. Ceram. Soc v.57 no.4 Use of the Notched-Beam Test for Evaluation of Fracture Energies of ceramics L. A. Simpson
  9. J. Am. Ceram. Soc v.56 no.1 Effect of Microstiucture on Measurements of Fracture Encrgy of Al₂O₃ L.A. Simpson
  10. Am. Ceram. Soc. Bull. v.46 no.11 Wire-Saw Outting Technique for Optical Crystals M.C. Huffstutler;J.R.;Becky T. Kerns
  11. The. Am. Ceram. Soc. System ZrO₂-Na₂O.SiO₂Phase Diagrams for Cermists J.D' Aus;J. Loffler
  12. Phase diagram for Ceramists. The. Am. Ceram. Soc. Liquidus curve of System Fe₂O₃-ZrO₂ H. Von Wartenberg;W. Eurr
  13. Am. Soc. Tes. Mat. Spec no.410 Plane Strain Crack Toughness Testing of high-strength Metallic Materials W.F. Brown;J.E. Srawley
  14. J. Am. Ceram. Soc. v.57 no.8 Fracture Toughness;Spalling Bchavior of High.Al₂O₃Refractories K.R. Larson;J.A. Coppola;D.P.H. Hasselmen