The Influence of Admixture of Lignosulfonic Acid Type on the Strength of Mortar

Lignosulfonic Acid계(系) 감수제(減水劑)가 모르터의 강도(强度)에 미치는 영향(影響)

This study is intended to find out the influence of Lignosulfonic Acid Type Admixture on compressive, tensile, flexural strength and dispersing action of mortar, and fixation of by-product of pulp industry. 1. The more Pozzolith-84 is added, the larger flow value is. The admixture of lignosulfonic acid type adhere to cement particles and the surface potential of particles is generated. On account of the repulsion among the cement particles, they are dispersed and the mortar get workable, so the production cost of precast product is curtailed and the amount of cement is reduced in a certain workability of mortar. 2. The strength of mortar is greater than plain mortar when P/C added is 0.2 and 0.4%. As time passed the potential energy is reduced and the distance of particles which lignosulfonic acid adhered to get near according as the amount of adhesion is increased. The setting and hardening reaction of morter is occurred in close state, so the strength of mortar is increased a little. The strength of mortar is less than plain mortar when amount P/C added is 0.8%. Pozzolith-84 is mainly composed of lignosulfonic acid and lignin does not influence the hardening of mortar, therefore the remained $SO_3$, $SO_3H$ are the reason of decrease of strength. 3. There is high significance between specific gravity and compressive strength. The larger specific gravity is, the more compressive strength is increased. There is high significance between 7 day's strength and 28 day's strength. The larger compressive strength is, the more tensile and flexural strength are increased. 4. Since Pozzolith-84 is a by-product of pulp industry, by using the Pozzolith-84 admixture the concreate quality is improved. The water pollusion is reduced according to fix by-products in concrete structure.

본(本) 연구(硏究)는 Lignosulfonic Acid계(系) 감수제(減水劑)를 첨가(添加)한 모르터의 유동성(流動性) 개선(改善)과 강도변화(强度變化)를 구명(究明)하고자 시행(施行)하였다. 1. Plastic 상태(狀態)에서 Pozzolith-84의 첨가량(添加量)을 늘리면 Flow가 증가(增加)하였다. 이는 Pozzolith-84의 첨가(添加) 시(時) 전기적(電氣的) 이중층(二重層)이 형성(形成)되어 시멘트 입자(粒子) 상호간(相互間)에 반발력(反撥力)이 생겨 분산(分散)된 것으로 이 분산작용(分散作用)은 술폰산기(酸基)의 계면활성작용(界面活性作用)에 기인(基因)되며, 시공성(施工性)이 개선(改善)됨에 따라 Precast 제품(製品) 생산(生産) 시(時) 비용절감(費用節減)의 효과(效果)가 있으며, 단위수량감소(單位水量減少)에 의(依)해 구조물(構造物)의 내구성(耐久性)이 개선(改善)된다. 2. 경화(硬化)된 상태(狀態)에서는 P/C가 0.2, 0.4%일 때 보통(普通)모르터의 강도(强度)보다 다소증가(多少增加)되었으며, P/C가 0.8% 이상(以上)일 때 보통(普通) 모르터의 강도(强度) 보다 감소(減少)된 것은 잔류(殘留) 술폰산(酸)($SO_3H$), 무수유산(無水硫酸)($SO_3$)의 화학반응(化學反應)에 의(依)한 것으로 생각된다. 3. 비중(比重)과 압축강도(壓縮强度) 분석(分析) 결과(結果) 고도(高度)의 유의성(有意性)이 있었으며 비중(比重)이 커짐에 따라 압축강도(壓縮强度)도 역시 증가(增加)되었고, 재령(材齡) 7일(日)과 28일(日)의 강도(强度) 분석(分析) 결과(結果) 고도(高度)의 유의성(有意性)이 있었으며, 재령(材齡) 7일(日)의 압축(壓縮) 강도(强度)가 클수록 인장(引張) 휩강도(强度)도 역시 크게 나타났다. 4. Pozzolith-84는 펄프공업(工業)의 폐기물(廢棄物)인 Lignosulfonic Acid Type이며 이를 실용화(實用化)하면 산업폐기물(産業廢棄物)의 활용(活用)에 유익(有益)하다고 생각된다.