Abstract
'Shingo' pears were seal-packaged in polyethylene (PE) film with different thickness of 0.04. 0.06, 0.07, and 0.08mm and stored for five months in an experimental storehouse with the temperature varyine 0 to $7^{\circ}C$ and relative humidity varying 86 to 89%. The atmosphere in PE film bags was modified to 5-l4% oxygen with 3-5% carbon dioxide depending on the film thickness and the storage period. Packaging of pears with PE film effectively reduced the weight loss, which resulted in good appearance after 5 months' storage, while non-packaged pears showed a slight wilt. Decay occurrence was not significantly different among the treatments. but role browning occurred a little more in packaged lots than in non-packaged lot. The sensory panel rated the pears front 0.07mm-thick bag highest in flavor, texture, and juiciness, which might be due to the high sugar content and low titratable acidity. The firmness of pear flesh decreased with the stogare time and its change was found to be highly correlated with that of cellulase activity (correlation coefficient= -0.946). Thisresult indicated that cellulase might be one of the enzymes responsible for the softening of pear fruit during storage.
'신고' 품종의 배를 두께가 다른$(0.04{\sim}0.08mm)$ 폴리에틸렌 필름으로 밀봉하여 KAIST 제작 농가용 저장고에서 MA저장 가능성을 검토하였다. 저장 5개월 동안에 저장고 내의 온도는 $0{\sim}7^{\circ}C$ 범위에서 상대습도는 $86{\sim}89%$가 유지되었다. 저장기간중 포장 내의 산소농도는 $5{\sim}14%$, 이산화탄소 농도는 $3{\sim}5%$ 범위에서 변화되었다. 배의 부패율은 $1.5{\sim}3.0%$로 포장구와 '비포장구간에 차이가 별로 없었으나 중량감소의 경우 비포장구는 저장 5재월 만에 4.1%까지 중량이 감소되어 위조현상이 나타났고 필름 포장구의 배는 중량감소가 약 1%밖에 발생하지 않아서 외관상 좋은 품질이 유지되었다. 한편, 관능경사 결과 0.07mm 두께의 필름으로 포장되었던 배가 풍미, 조직감, 다즙성 면에서 가장 높은 선호도를 나타냈는데 이는 당도가 가장 높고 산도가 가장 낮았던데 기인한 듯하다. 저장기간이 경과함에 따라 과육의 경도는 계속 감소하는 경향을 보였으며 섬유소 가수분해효소의 활성은 증가되었는데 과일 경도의 감소와는 밀접한 상관관계(상관계수는 -0.946)를 나타내었다. 과일의 세포벽은 점차적인 붕괴현상을 나타내었는데 이는 섬유소 가수분해효소가 작용한 것으로 판단된다.