Abstract
The crystallization behaviour and the machinability of mica glass-ceramics with the content of F1 were studied. The material was made from the $K_2O-MgO-Al_2O_3-B_2O_3-SiO_2-F$ glasses by the heattreatment at 80$0^{\circ}C$-110$0^{\circ}C$ where the content of F-1 was changed in the range from 1, 3wt% to 6.1wt%. X-ray diffraction phase analysis and optical observation were adopted to study the crystallization behaviour. The machinability was measured by a manual sawing test and MOR. The crystal phases of these glass-ceramics identified by XRD were chondrodite fluoborite and norbergite at low temperature but fluorophlogopite at high temperature. The crystallization of glasses containing 1.3wt% -2.5wt% F-1 were predominately controlled by surface crystallization while the crystallization of glasses containing 3.8 wt% -6.1wt% F-1 were controlled by volume crystallization. Among the test the best machinability and strength value were obtained from those specimens contained fluoride 4.2wt% -4.4wt% and when the heattreatment was performed at 95$0^{\circ}C$-110$0^{\circ}C$ for 2 hours.