Crack growth behavior of fatigue surface crack initiated from a small surface defect

작은 表面缺陷에서 發생.成長하는 表面疲勞균열의 成長特性에 관한 硏究

It has been well known that the fracture mechanics can be applied to large through crack growth. But the growth rate of small surface cracks initiated from a small defect under rotary bending fatigue tests can not be treated as a function of stress intensity factor range. In this paper, to investigate the growth behavior of surface small fatigue cracks in the view-point of both fracture mechanics and strength of materials, the fatigue test has been carried out on two kinds of plain carbon steels with a small surface defect. Applying the concept of the cyclic strain intensity factor range .DELTA. $K_{\epsilon}$/$_{t}$ to the analysis of small surface fatigue crack growth, it is found that the relationship between cyclic strain intensity factor range and crack growth rate shows linear relation on logarithmic coordinates regardless of defect sizes and two kinds of carbon steels.s.s.

본 논문에서는 이상과 같이 그 중요성이 인정되는 작은 표면피로균열의 성장 특성을 조사하기 위하여 연강과 중탄소강에 두 종류의 작은 표면결함을 가공한 네가지 종류의 시험편을 제작하고, 응력비 R=-1인 소야식 회전굽힘 피로시험을 통하여 작은 표면결함이 피로강도에 미치는 영향과 그 성장특성을 조사한 후 응력확대계수 K를 사 용하는 방법과 반복전스트레인 확대계수범위 .DELTA. $K_{\epsilon}$t/를 비교 검토하여 그 유효성 을 조사하고 이를 파괴역학적 측면에서 고찰하였다.다.