시멘트 클린커 광물의 수화에 미치는 해수성분의 영향 (I)SO42- 및 Cl-이온에 의한 영향

The Effect of Seawater on Hydration of Clinker Minerals (I) Effects of SO42- and Cl- ions

  • 신도철 (인하대학교 무기재료공학과) ;
  • 송태웅 (인하대학교 무기재료공학과) ;
  • 한기성 (인하대학교 무기재료공학과) ;
  • 최상흘 (한양대학교 무기재료공학과)
  • 발행 : 1987.01.01

초록

Hardened cement paste is mainly affected by corrosion of sulphate and chlorine ions in sea water. In this investigation, many specimens were made with the cement clinker minerals such as C3S, C3A, C4AF and their mixture according to cement composition added various blending materials. After the specimens were immersed in 4% MgSO4 and MgCl2 solutions, the product of reaction, the microstructure of specimen and Ca+2 ion leached in the solution were studied. The formation of Ca(OH)2 in the specimen of C3S is reduced relatively by adding pozzolanic admixtures. The chlorine ion is easily diffuse into the C3S specimen and produced CaCl2 compound, and it makes the specimen porous by leaching out itself into the solution. The specimen of C3A, C4AF are broken down by expanding reaction of ettringite and gypsum compound produced in the MgSO4 solution. At a later period, the ettringite is transformed into gypsum and 5MgO.2Al2O3·15H2O. The C3A in the MgCl2 solution combines chlorine ion to form Friedel's salt and prevents the diffusion reaction of chlorine ion into the specimen. Granulated slag shows inferior effect on the resistance of the specimen in MgSO4 solution by forming ettringite and gypsum, but good result in MgCl2 solution. Pozzolanic materials, on the whole, offer noticable effect on the resistance of the specimen in both solutions.

키워드

참고문헌

  1. セ技年報 v.28 各種セメントの 耐硫酸性に關する硏究 小林和一;岡林茂生;片岡信裕
  2. Cem. Con. Res. v.2 Concrete for Long Time Service in Sulfate Environment G. L. Kalousek;L. C. Porter;E. J. Benton
  3. 7th Int. Symp. Chem. Cem. v.4 Mechanism of Sulfate Exposition S. Chatterji
  4. セ技年報 v.34 ミネラライザ一に よる 耐硫酸?性の付與に 關する 2, 3の 實驗 田中光男;況田正志;柴岡貞男
  5. 4th Int. Sym. Chem. Cen. v.4 Chemical Resistivities of Various Types of Cement R. Kondo
  6. セメント·ユンリ一ト no.345 各種セメントの?化物抵抗性 鈴川論一;小林和一;岡林茂生
  7. Cem. Con. Res. v.15 The Combined Action of Mg and Cl¨ ions in Cement Pastes C. Ftikos;G. Parssakis
  8. Cem. Con. Res. v.15 Resistance of Mortars Containing Silica Fume to Attack by a Solution Containing Chlorids R. F. Feldman;Huang Chong-Yi
  9. 5th Int. Symp. Chem. Cen. v.3 Chloride Reaction of Strong Chloride Solutions With Concrete H. G. Smolczyk
  10. セ技年報 v.33 セメントの 化學抵抗性に關する 硏究 小林和一;岡林茂生
  11. セ技年報 v.32 セメント硬化體に 與える 海水の 化學的 侵蝕カニズム 尾野論也;永嶋正久;大塚邦夫;伊藤隆明
  12. ACI Journal v.67 Mechamism of Seawater attack on Cement Pastes G. L. Kalousk;E. J. Benton
  13. セメント·ユンリ一ト v.433 海水中の?索成分は ユンリ一トにどの程度侵透おるか セメント協會
  14. セ技年報 v.30 セメント硬化體中における 硫酸根の擴散 牛山宏隆;岩倉博之;福永海安
  15. 最新 ユンリ一ト技術選書 v.6 ユンリ一トの耐海水性 關博;大友忠典
  16. Cem. Con. Res. v.2 Studies on Blended Portland Cements Containing Santorian Earth P. K. Metha
  17. セメント·ユンリ一トの化學 秋山柱一
  18. 8th Int. Symp. Chem. Cem. v.4 Dissociation of Al from Slag Glasses and Formation of Ettringite Lou zonghan;XU Xianyu;YANG Liqun;SHENG Qizhong
  19. 近勝連一先生 追悼記念誌 高爐スラグの利用について 官人英彦
  20. Application of Differential Thermal Analysis in Cement Chemistry V. S. Ramachandran
  21. 7th Int. Symp. Chem. Cem. v.4 A Study on the Action of Sea water on Hydrated Cement Pastes C. Ftikos;V. Kasselouris;G. Parissakis