Optimum Reaction Kinetics Model of Heat-resistant and Flame-Retardant Polymethyl Methacrylate

내열 및 난연성 Polymethyl Methacrylate의 최적 반응속도 모델에 관한 연구

  • Kim, Dong-Keun (Department of Chemical Engineering, College of Engineering, Dong-A University) ;
  • Seul, Soo-Duk (Department of Chemical Engineering, College of Engineering, Dong-A University) ;
  • Sohn, Jin-Eon (Department of Chemical Engineering, College of Engineering, Dong-A University)
  • 김동건 (동아대학교 공과대학 화학공학과) ;
  • 설수덕 (동아대학교 공과대학 화학공학과) ;
  • 손진언 (동아대학교 공과대학 화학공학과)
  • Published : 1987.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

The thermal degradation of the homopolymer poly(methyl methacrylate) (PMMA) and flame-retardant tetrabrormobisphenol-A(TBBA) as well as of their blends were carried out using the thermogravimetric method in the stream of nitrogen gas with 60ml/min at various heating rate from 1 to $20^{\circ}C/min$. Friedman and Ozawa mathematical methods were used to obtain the value of activation energy.

PMMA와 TBBA의 혼합비를 변화시킨 시료를 질소기류 하에서 비등온 열중량 분석법으로 가열속도 $1-20^{\circ}C/min$, 등온분해온도 $200-300^{\circ}C$로 열분해시킨 시료를 적외선 분광분석한 결과 TBBA의 함량 증가에 따라 활성화에너지 값은 Friedman법으로 28-46 Kcal/mol, Ozawa법으로 28-38 Kcal/mol로 증가 하였다. PMMA에 TBBA의 첨가에 따른 열분해반응은 주쇄 분해반응으로 이루어지며 실제 열중량곡선과 거의 일치되는 최적의 분해반응 모델식을 산출할 수 있었다.