Sorption Characteristics of Binary Mixture of Corn Starch- Soy Protein Isolates in Plastic film Packaging

Plastic필름 포장에 따른 옥수수 전분과 분리 대두단백질의 이성분 혼합물의 흡습특성

Sorption properties of corn starch(CS) and Soy protein isolates(SPI) in plastic films packaging were investigates for binary system. The mixture were sealed in plastic films of low density polyethylene(LDPE), oriented polypropylene(OPP) and LDPE/OPP coated film and packaging effect on the changes of moisture sorption during storage at $40^{\circ}C$ were studied. The following results were obtained. The water vapor permeability of material films was $32.6g/m^2/24hrs(below\;g)$ for 0.02mm LDPE film, 14.01g for 0.04mm LDPE film, 7.30g for 0.02mm OPP film, 3.37g for 0.04mm OPP film and 4.869 for 0.02mm LDPE/0.02 mm OPP confine film at $40^{\cire}C$ 90%RH, therefore the OPP film was more effective than LDPE film on the resistance of relative humidity. And the OPP film packaging sealed mixture of food samples was also more elective then LDPE film, having same thickness for increase of water vapor permeability during storage at $40^{\cire}C$. A general increase in sorption rate was found more in SPI than CS in the packaged mixtures.

전분가공식품의 주요 원료인 옥수수전분과 단백질강화 또는 육란백질의 대치 단백질인 분리대두단백질을 사료로 하여 전분-단백질의 이성분혼합비율을 오늘날 흔히 사용되고 있는 plastic flim으로 포장하여 상대습도 90%와 $40^{\circ}C$에서 포장재료의 성질이 흡습특성에 미치는 영향을 조사하였다. 포장재료별 투습도는 0.02mm LDPE필름이 $32.6g/m^2/24hrs$ 0.04mm LDPE필름이 $14.01g/m^2/24hrs,$ 0.02mm OPP 필름이 $7.30g/m^2/24hrs,$ 그리고 0.02mm LDPE /0.02 mmOPP coating필름이 $4.86g/m^2/24hrs,$로서 동일한 두께성에서 비교해 볼 때 LDPE필름보다 OPP필름이 습기의 차단성이 대략 4배이상 우수함을 알 수 있었다. 또 식품시료를 포장하여 저장하는 경우도 동일한 두께의 LDPE필름보다 OPP필름이 습기의 차단성이 우수하였다. 그리고 포장한 혼합물의 저장시간에 따른 흡습속도는 일반적으로 전분함량보다는 단백질함량이 많을수록 흡습속도가 크게 증가하는 것을 알 수 있었다.