오스테나이트계 스테인레스강의 육성 용접부에서 고온균열 감수성에 미치는 용접입열의 영향

  • 김대영 (현대중공업(주) 용접기술연구소) ;
  • 김희진 (현대중공업(주) 용접기술연구소)
  • Published : 1988.06.01

Abstract

The effect of heat input on the content of residual .delta.-ferrite and the hot cracking susceptibility in the austenitic stainless steel overlaid on the carbon steel was studied in the range of heat input from 7.5 to 15.1 KJ/cm. Present study shows that residual .delta.-ferrite content in the overlay is mainly determined by the dilution of the base metal (carbon steel) which is in turn affected by heat input, i.e. the amount of dilution decreases as heat input increase. Accordingly, higher heat input results in a substantial increase in Cr equivalent but a little increase in Ni equivalent due to the less dilution of carbon from base metal. This fact can explain the result obtained in this study, i, e, the higher content of .delta.-ferrite in the weld deposit made with higher heat input. This in turn causes more resistant overlaying weld metal to hot cracking.