Preparation of Al2O3-ZrO2 Composite Powders by the Use of mulsions : II. Emulsion-Hot Kerosene Drying Method

에멀젼을 이용한 Al2O3-ZrO2 복합분체의 제조 : II. 에멀젼-가열석유 증발법

  • 현상훈 (연세대학교 요업공학과) ;
  • 백종규 (연세대학교 요업공학과)
  • Published : 1988.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Alumina-zirconia composite powders for the purpose of improving fracture toughness and thermal shock resistance of alumina were prepared by the emulsion-kerosene drying method. The average particle size of composite powders was less then 1 $\mu\textrm{m}$ and their shapes were spherical. It was shown that the average particle size of composite powders decreased with the concentration of metal-salt in solution and the amount of span 80 added when preparing emulsions. The structure of all zirconia in composite powders heat-treated at 1200$^{\circ}C$ was a tetragonal form at room temperature. This result implied that fine zirconia particles were homogeneously dispersed in the alumina matrix.

Keywords

References

  1. J. Am. Ceram. Soc. v.59 no.1-2 Fracture Toughness of Al₂O₃with an Unstabilized ZrO₂Dispersed Phase N. Claussen
  2. J. Am. Ceram. Soc. v.61 no.1-2 Stress-Induced Transformation of Tetragonal ZrO₂Particles in Ceramic Matrices N. Claussen
  3. J. Mat. Sci. v.17 no.1 Transformation Toughening F.F. Lange
  4. Am. Ceram. Soc. Bull. v.60 no.2 Nonconventional Powder Preparation Techniques D.W. Johnson, Jr.
  5. Ceramic Powder The Use of Emulsions in the Preparation of Ceramic Powders P. Reynen;H. Bastius;M. Fiedler;P. Vincenzini(ed.)
  6. J. Korean Ceramic Society v.24 no.6 Preparation of Al₂O₃-ZrO₂Composite Powders by the Use of Emulsions:Ⅰ. Thermodynamic Model of the Emulsion Stability S.H. Hyun;J.G. Paik;S.R. Song
  7. J. Am. Ceram. Soc. v.67 no.5 Preparation of Alumina-Zirconia Powders by Evaporative Decomposition of Solutions D.W. Spronson;G.L. Messing
  8. Better Ceramics Through Chemistry Ⅱ Preparation of Ceramic Powders from Emulsions M. Akinc;K. Richardson;C.J. Brinker(ed.);D.R. Ulrich(ed.);D.E. Clark(ed.)
  9. J. Phy. chem. v.69 no.4 The Occurrence of Metastable Tetragonal Zirconia as a Crystallite Size Effect R.C. Garvie
  10. J. Am. Ceram. Soc. v.45 no.12 Effect of Pressure on Mono-clinic-Tetragonal Transition of Zirconia: Thermodynamics E.D. Whitney