Li2O-Al2O3-SiO2계 결정화 유리의 특성(I)

Properties of Li2O-Al2O3-SiO2 Glass Ceramic System(I)

  • 발행 : 1988.05.01

초록

The properties of scid-resistance to boiling HCl, thermal expansion coefficient and softening temperature of mother glass and glass-ceramic of LAS systems were investigated at the contents of SiO2 varing from 57 to 67wt%. The nucleation and growth of crystalline phase of LAS compositions were carried out at 50$0^{\circ}C$ and $700^{\circ}C$. The crystalline phase jconsists of lithium alumino silicate, lithum meta silicate, lithium disilicate, $\alpha$-crystobalite and $\alpha$-quartz. Lithium alumino silicate(virgilite) is the major crystalline phase in the glass ceramics. The degree of acid resistant property was increased in proportion with the silica content for both glass and ceramics. Glass-ceramic gives lower acid-resistance and thermal expansion coefficient while softening temperature shows higher for glass-ceramic than for mother glass.

키워드

참고문헌

  1. Sprechsoal Keram, Glass Email Silikate v.102 no.24 Glaser des Systems R₂O-Al₂O₃-SiO₂als Grudlage der Saurebestandigen Emails W. W. Wargin;W. E. Mischel
  2. The Vitreous Enameller v.34 no.21 Improved Enamels for Chemical Plant G. Partridge
  3. Ceramic Proceeding Glass Ceramic Enamels for High Temperature Applications W. D. Faust
  4. Werkstoffe und Korrosion v.30 Use of Non-Metallic Materials for Reducing Corrosion Damage Von H. Grafen(et al.)
  5. Ceramic Proceeding Reactions at Glass-Ceramic to Metal Interfaces R. E. Loehman(et al.)
  6. DIN 12116 Prufung von Glass Bestimmung der Saurebestandigkeit und Einteilung der Glaser nach Saureklassen
  7. ASTM C372 Linear Thermal Expansion of Porcelain Enamel and Glaze Frits and Fired Ceramic Whiteware Products by the Dilatometer Method
  8. ASTM C338 Test Method for softening Point of Glass
  9. Jour. of. Mat. Sci v.19 no.12 Nucleation Kinetics in a Glass-Ceramic Enamel J. Penkov;I. Gutzow
  10. Jour. of. Am. Cer. Soc v.46 no.12 Glass Fotmation and Recrystallization in the Lithium Metasilicate Region of the System Li₂O-Al₂O₃-SiO₂ R. A. Eppler