Oxygen Index Evaluation of Wood-Based Materials

산소지수법(酸素指數法)에 의(依)한 목질판상재료(木質板狀材料)의 연소시험(燃燒試驗)

The oxygen index test was carried out to obtain the relative flammability of wood-based materials (plywood, MDF, particleboard) and their oxygen indices. The oxygen index is the minimum concentration of oxygen, expressed as volume percent, in a mixture of oxygen and nitrogen that will just support flaming combustion of a material under the specified laboratory conditions. In this study the oxygen indices were calculated by using the Dixon and Massey's Up and Down method("N" Large method). The obtained results were as follows : 1. The oxygen indices calculated with Up and Down method were 27.9% for plywood, 26.9% for MDF, and 26.2% for particleboard, indicative of plywood being more difficult to burn than MDF and particleboard Lender the same surrounding conditions. 2. The oxygen indices were not affected by the total gas flow rate.

본(本) 시험(試驗)은 산소지수법(酸素指數法)에 사용(使用)하여 목질판상재료(木質板狀材料)의 상대적(相對的) 연소성(燃燒性)과 그들의 산소지수(酸素指數)를 알아보기 위하여 수행(遂行)되었다. 산소지수(酸素指數)는 일정비율(一定比率) 산소(酸素), 질소(窒素) 혼합기체(混合氣體)의 흐름속에서 재료(材料)가 발염연소(發炎燃燒)를 지속(持續)할 수 있는 최소(最少) 산소농도(酸素濃度)를 말한다. 본(本) 시험(試驗)에서는 산소지수(酸素指數)를 계산(計算)하기 위하여 Dixon과 Massey의 Up and Down법(法)을 사용(使用)하였으며 그 결과(結果)를 요약(要約)하면 다음과 같다. 1. 산소지수(酸素指數)는 합판(合板)이 27.9%로 가장 높게 나타났으며, MDF와 파티클보드의 산소지수(酸素指數)는 각각 26.9%와 26.2%이었다. 이것은 합판(合板)이 MDF나 파티클보드에 비해 난연소성(難燃燒性)을 가지고 있는 것을 나타낸다. 2. 산소지수(酸素指數)는 혼합기체유동속도(混合氣體流動速度)에 의하여 영향(影響)을 받지 않았다.